test description | test method |
tape adhesion | astm d3359; fltm bi 106-01; gm 9071p; |
water immersion | astm d870; fltm bi 104-01; gm 4466p; hes d6501 sec. 3.18 & 3.37, s84 sec. 6.7; tsh 1551g |
gravelometer/chip | astm d3170; gm 9508p method b; hes d6501 sec. 3.33; sae j400; tsh 1553g; delphi dx 900163 |
humidity | astm d1735, d2247; gm 4465p, w3044 & w4700 (label compatibility); hes d6501 sec.3.19, s84 sec. 6.8; sae-ams-std 753c method 101; tsh 1505g; din 50017 |
spray | astm b117; gm 4298p; fltm bi 103-01; hes d6001 sec. 4.3, d6501 sec. 3.15.1 & 2; iso 7253, 9227; jaso m610; jis z2371; mil-std 810 (salt spray section); nes m0140; tsh 1552g; din50021; jis h8502 sec. 7.1 |
20% salt spray | astm c1503 |
pencil hardness (w/ d3363 pencils) | astm d3363; hes d6501 sec. 3.5, s84 sec. 6-4; tsh 1500g |
dime scrape | gm 9506p |
film thickness | astm d1186, d1400; fltm bi 117-01 |
thumbnail hardness | gm 9507p |
solvent rub | astm d5402, gm 9509p, tsh 1551g sec 5.2 |
cyclic corrosion | chrysler lp-463pb-22-01; delphi dx900115; fltm bi 123-01; gm 9505p cycles a-o, 9511p, 9540p, 9619p; gm w14872; sae j2334; vda 621-415; nes m0158, cct-i, cct-iv |
chipping corrosion | chrysler lp-463pb-52-01 |
modified salt fog | astm g85 annex 1, 2, 3 & 5 |
c.a.s.s. | astm b368; fltm bq 105-01; gm 4476p; jis h8502 sec. 7.3 |
so2 | astm g87; din 50018 |
corrodkote | astm b380; hes d6001 ref. 1 |
uv (quv) exposure | astm d4587; g154; sae j2020 |
cyclic salt fog/uv exposure | astm d5894 |
filiform | astm d 2803 procedures a-c; gm 9682p; hes d6501 sec. 3.16 |
rating & evaluation | astm b537, d610, d714, d1654; gm 9102p |
temperature | ford wss-m2p177-a1-5 sec. 3.5.7; hes d6001 sec. 4.4.1, d6501 sec. 3.20.1&2; tsh 1551g sec. 9 |
thermal shock | fford wsb-m1p83-b1 sec. 3.8.2; gm 4372m sec. 3.5.2; hes d6001 sec. 4.4.4, d6501 sec. 3.29; tsh1551g |
heat/quench | delphi dx551200,dx551300; gm w3044, w4700 |
ph | astm d1293 |
conductivity | astm d1125 |
specific gravity | astm d1429 |
salt water immersion | chrysler ms-pb1-2 |